1.2367 (X38CrMoV5-3) Tool Steel

1.2367 (X38CrMoV5-3) material is a hot work tool steel developed as an alternative to 1.2365, specifically chosen for applications requiring high temperature resistance. It provides both higher hardness and better wear resistance compared to 1.2365.

Product Shape

Flat Bar Diameter

Piece(s)

What is 1.2367 (X38CrMoV5-3) (DM3X) Steel?

1.2367 (X38CrMoV5-3) material is a hot work tool steel developed as an alternative to 1.2365, specifically chosen for applications requiring high temperature resistance. It provides both higher hardness and better wear resistance compared to 1.2365.

The mechanical properties of 1.2367 (X38CrMoV5-3) hot work tool steel at high temperatures are superior to those of 1.2343 and 1.2344. For instance, it offers a longer working lifespan in copper and brass extrusion molds compared to others. 1.2367 (X38CrMoV5-3) hot work tool steel is also produced using the EFS and ESR methods.

What is the Hardness Value of 1.2367 (X38CrMoV5-3) (DM3X) Steel?

The hardness value of 1.2367 (X38CrMoV5-3) hot work tool steel is between 46-54 HRC. The usage hardness can be 1-2 HRC higher.

What are the Mechanical Properties of 1.2367 (X38CrMoV5-3) (DM3X) Steel?

You can find the material properties of 1.2367 (X38CrMoV5-3) in the "Technical Details" tab. All mechanical and material properties of 1.2367 (X38CrMoV5-3) steel are specified within this tab.

Where is 1.2367 (X38CrMoV5-3) (DM3X) Steel Used?

1.2367 (X38CrMoV5-3) hot work tool steel can be used with superior performance in all applications where 1.2365 steel is used. 1.2367 (X38CrMoV5-3) tool steel is used as an extrusion press container in the extrusion pressing of metals like copper and brass, in embossing thrust shafts and molds, as cores in hot forging molds, in metal injection molds, in water-cooled hot shear blades, and in the production of hot products like bolts and nuts.

The 2% more of chromium in 1.2367 (X38CrMoV5-3) material results in less wear at high temperatures. Chromium enhances wear resistance but reduces thermal conductivity. If heat transfer and thermal resistance are more critical than wear, the 1.2365 (32CrMoV12-28) hot work tool steel with lower chromium content should be used.

What is the Price of 1.2367 (X38CrMoV5-3) (DM3X) Material?

The price of 1.2367 (X38CrMoV5-3) material varies depending on the product section, dimensions, and surface quality. You can access 1.2367 (X38CrMoV5-3) steel prices through the "Proceed to Online Sales" button on the www.saglammetal.com homepage.

Chemical Composition

Code: 1.2367, DM3X, X38CrMoV5-3

Carbon	Chromium	Molybdenum	Vanadium
C	Cr	Mo	V
0,38	5,00	3,00	0,50

Heat Treatment

	Temperature	Cooling	Hardness
Soft Annealing	730 - 780 °C	Furnace	229 HB
Stress Relief Annealing	600 - 650°C	Furnace
Hardening	1030 - 1080°C	oil, pressure gas (N2), air or hot bath 500 - 550°C	see tempering diagram

Mechanical Properties

Hardness

46 - 54

HRC

Physical Properties

Thermal Expansion Coefficient	11,9 - 13,5	1/K * 10^-6
Thermal Conductivity (20°C)	30,8	W/mK
Density	7,85	g/cm³

1.2367 (X38CrMoV5-3) Tool Steel