1.2714 (55NiCrMoV7) Tool Steel

1.2714 (55NiCrMoV7) material is a medium to large scale hot work tool steel that is nickel-alloyed, has excellent toughness, and can be hardened to the core.

SHOW PRICES

What is 1.2714 (55NiCrMoV7) (A50) Steel?

1.2714 (55NiCrMoV7) material is a medium to large scale hot work tool steel that is nickel-alloyed, has excellent toughness, and can be hardened to the core. It can be delivered in both hardened and tempered conditions. However, there is a risk of fracture when working at hardness levels above 52 HRC. Therefore, for shallow molds where 1.2714 (55NiCrMoV7) is insufficient, 1.2344 or 1.2367 grade steels should be preferred.

What is the Hardness Value of 1.2714 (55NiCrMoV7) (A50) Steel?

The hardness value of 1.2714 (55NiCrMoV7) hot work tool steel is between 37-50 HRC.

What are the Mechanical Properties of 1.2714 (55NiCrMoV7) (A50) Steel?

You can find the material properties of 1.2714 (55NiCrMoV7) in the "Technical Details" tab. All mechanical and material properties of 1.2714 (55NiCrMoV7) steel are specified within this tab.

Where is 1.2714 (55NiCrMoV7) (A50) Steel Used?

1.2714 (55NiCrMoV7) tool steel is used in the production of stainless-steel goods, base forging dies, multipart pressing molds, punch dies for extrusion presses, supports for seal carriers, casings, and hot shear blades. For hot cutting applications in rolling mills and flying shear blades, it is recommended to use WP7V material due to its high wear resistance.

What is the Price of 1.2714 (55NiCrMoV7) (A50) Material?

The price of 1.2714 (55NiCrMoV7) material varies depending on the product section, dimensions, and surface quality. You can access 1.2714 (55NiCrMoV7) steel prices through the "Proceed to Online Sales" button on the www.saglammetal.com homepage.

Chemical Composition

Code:1.2714, A50, 55NiCrMoV7, AISI: L6

Carbon	Chromium	Molybdenum	Nickel	Vanadium
C	Cr	Mo	Ni	V
0,55	1,10	0,50	1,70	0,10

Heat Treatment

	Temperature	Cooling	Hardness
Soft Annealing	650 - 700 °C	Fırın	248 HB
Stress Relief Annealing	600 - 650°C	Fırın
Hardening	840 - 890°C	oil, pressure gas (N2), air	air see tempering diagram

Mechanical Properties

Hardness

37 - 42

HRC

Physical Properties

Thermal Expansion Coefficient	12,3 - 14,4	1/K * 10^-6
Thermal Conductivity (20°C)	35,9	W/mK
Density	7,85	g/cm³

1.2714 (55NiCrMoV7) Tool Steel